Versatile Zirconia Puck Fabrication Application
The puck is used for a wide of versatile clinical application, from veneer to large spans. The flexutrual strength, translucency, and pre-shaded integrate into one single puck seamlessly.
High strength and translucency in a natural transition:
3Y-5Y Multilayer Strength & Translucency Gradient in Balance Design Features:
Translucency: Progressive transition from 49% (incisal / enamel zone) to 40% (cervical / dentin zone). This range provides sufficient light transmission for natural vitality and depth in the visible areas while maintaining enough opacity cervically to mask underlying structures when needed.
Strength: Progressive transition from 600 MPa (more translucent incisal zone) to 1200 MPa (higher-density cervical / body zone). The higher-strength region is strategically located where functional stresses (bending and tensile forces) are greatest, while the lower-strength but higher-translucency region prioritizes aesthetics where the eye focuses.
Clinical versatility: One material class covers both high-aesthetic anterior cases (leveraging the 49% zone) and posterior load-bearing cases (leveraging the 1200 MPa zone), simplifying material selection and improving patient outcomes with natural-looking, durable results. Implant restorations and selected full-arch frameworks – benefit from the overall high strength envelope and stable sintering behavior.
Flexural Strength
| LAYERS; | LAYER PROPORTION | FLEXURAL STRENGTH |
| 1st Layer (light Shade) | 20% | >=600MPA |
| 2ed Layer | 15% | >=720MPA |
| 3rd Layer | 15% | >=840MPA |
| 4th Layer | 15% | >=960MPA |
| 5th Layer | 15% | >=1080MPA |
| 6th Layer | 20% | >=1200MPA |
It is suitable for all types of zirconia-based restoration cases, and idea for anterior, posterior, and long spans framework restoration due to high bending strength.
Application: For veneers, implants, Inlay, Onlay, Posterior, anterior crown, and bridge
Sintering Program